Low energy mechanical treatment of non-stoichiometric titanium carbide powder

OBRABOTKAMETALLOV MATERIAL SCIENCE Vol. 23 No. 3 2021 Fig. 4. Fragments of the X-ray diffraction patterns of planes (111) ( a , c ) and (511) ( b , d ) of the powder in the initial state ( a , b ) and that after mechanical treatment ( c , d ) a b c d Fig. 5. CDD size (a) and crystal lattice microdistortions (b) vs. mechanical treatment time for two structural states TiC 0.65 and TiC 0.48 a b