Study of the effect of hafnium and erbium content on the formation of microstructure in aluminium alloy 1590 cast into a copper chill mold

ОБРАБОТКА МЕТАЛЛОВ Том 26 № 1 2024 104 МАТЕРИАЛОВЕДЕНИЕ Рис. 2. Микроструктура исследуемых образцов из сплавов: а – 1590; б – 1590Er0,03Hf0,05; в – 1590Er0,03Hf0,1; г – 1590Er0,03Hf0,16; д –1590Er0,1Hf0,05; е – 1590Er0,1Hf0,1; ж – 1590Er0,1Hf0,16; з – 1590Er0,16Hf0,05; и – 1590Er0,16Hf0,1; к – 1590Er0,16Hf0,16 (см. также с. 105) Fig. 2. Microstructure of the studied alloy specimens: a – 1590; б – 1590 Er0.03-Hf0.05; в – 1590 Er0.03-Hf0.1; г – 1590 Er0.03-Hf0.16; д – 1590 Er0.1-Hf0.05; е – 1590 Er0.1-Hf0.1; ж – 1590 Er0.1-Hf0.16; з – 1590 Er0.16-Hf0.05; и – 1590 Er0.16-Hf0.1; к – 1590 Er0.16-Hf0.16 (see also p. 105) а б в г д е