Structural features and tribological properties of multilayer high-temperature plasma coatings

OBRABOTKAMETALLOV MATERIAL SCIENCE Vol. 26 No. 3 2024 Fig. 9. Coating B surfaces after sliding friction tests: a – load 30 N; b – load 75 N; c – load 100 N; d – load 130 N a b c d Ta b l e 6 Chemical composition of the wear surface of the coating А, at. % Load Fe O Cr Mn Si B C 30 N 56.30 4.87 0.23 0.11 0.14 7.15 4.87 75 N 47.45 4.63 0.72 0.24 0.54 7.41 4.63 100 N 63.03 9.63 2.42 1.15 1.84 11.40 8.00 130 N 57.63 13.23 2.74 1.30 1.87 13.24 6.87 Ta b l e 7 Chemical composition of the wear surface of the coating B, at. % Load Fe O Ni Mn Si B C 30 N 60.59 38.02 0.13 0.20 0.17 0.00 0.00 75 N 61.67 29.34 3.91 1.94 1.47 2.19 1.07 100 N 61.06 28.25 4.80 2.17 1.76 2.46 1.48 130 N 59.36 28.13 6.28 2.28 1.72 4.07 1.00