OBRABOTKAMETALLOV MATERIAL SCIENCE Vol. 26 No. 4 2024 Fig. 4. Micro X-ray spectral analysis of specimens after 80 % deformation: a – shooting surface; b – B distribution; c – Cr distribution; d – Fe distribution; e – Ni distribution а b c d e Fig. 5. Specimens after synchrotron radiation diff raction case, it is necessary to note a decrease in the intensity of boride peaks relative to the intensity of austenite peaks and the textured nature of its distribution in the austenite matrix, as well as an increase in the intensity of diff raction peaks 200 and 202 at 30 % degree of deformation. In the process after non-vacuum electron beam surfacing and subsequent plastic deformation, a texture is present, which means that the specimens