Obrabotka Metallov 2012 No. 4

ОБРАБОТКА МЕТАЛЛОВ № 4 (57) 2012 78 МАТЕРИАЛОВЕДЕНИЕ Structural-phase composition of the Fe-contained alloyed, modified with ultra- and nanodispersed powders of d-metals oxides A.P. Zykova, M.Yu. Novomeyskiy, I.A. Kurzina, A.A. Nikulina, A.S. Knyazev Methods of X-ray analysis and scanning electron microscopy were used to study iron C425 in tree states: 1) without the addition of a modifier mixture (MS); 2) after the introduction of MS (mixture of ultra- and nanopowder metal oxides d-metals with a reducing cryolite (Na 3 AlF 6 ) and 3) after the introduction of MS with calcium carbide (CaC 2 ). The element composition, phase composition, microstructure studied metal matrix and graphite inclusions. It was established that the introduction of the modifying mixture with a reducing agent (Na 3 AlF 6 or CaC 2 ) leads to a morphologically homogeneous structure, changes in the phase composition, the content of the volume fraction of the phases, the crystal lattice of solid solutions. Key words: Iron GL25, modification, ultra- and nano-dispersed oxide powder, phase composition, lattice parameter, and microstructure. 3. Семенихин Б.А., Петридис А.В., Куприяно- ва И.Ю. Возможность использования комплексно- го модификатора длительного действия на основе нанопорошков для повышения качества отливок из алюминиевых сплавов // «Новые материалы и тех- нологии в машиностроении – 2005». IV Междуна- родная научно-техническая конференция, 2005. – С. 342–344. 4. Модификатор МС // Технические условия 1760-001-64101572-2011. 5. ГОСТ 3443-87. Отливки из чугуна с различной формой графита. Методы определения структуры // Межгосударственный стандарт, 2005. – М., 2005. – 43 с. 6. База рентгеноструктурных данных PDF-4. 7. Диаграммы состояния двойных металлических систем / под ред. Н.П. Лякишева. – М.: Машиностро- ение, 1996. – Т. 1–3.