OBRABOTKAMETALLOV Vol. 27 No. 2 2025 253 MATERIAL SCIENCE Eff ect of impact processing on the structure and properties of nickel alloy ZhS6U produced by casting and electron beam additive manufacturing Andrey Vorontsov a, *, Alexander Panfi lov b, Alexandra Nikolaeva c, Andrey Cheremnov d, Evgeny Knyazhev d Institute of Strength Physics and Materials Sciences SB RAS, 2/4, pr. Akademicheskii, Tomsk, 634055, Russian Federation a https://orcid.org/0000-0002-4334-7616, vav@ispms.ru; b https://orcid.org/0000-0001-8648-0743, alexpl@ispms.tsc.ru; c https://orcid.org/0000-0001-8708-8540, nikolaeva@ispms.tsc.ru; d https://orcid.org/0000-0003-2225-8232, amc@ispms.ru; e https://orcid.org/0000-0002-1984-9720, clothoid@ispms.tsc.ru Obrabotka metallov - Metal Working and Material Science Journal homepage: http://journals.nstu.ru/obrabotka_metallov Obrabotka metallov (tekhnologiya, oborudovanie, instrumenty) = Metal Working and Material Science. 2025 vol. 27 no. 2 pp. 238–254 ISSN: 1994-6309 (print) / 2541-819X (online) DOI: 10.17212/1994-6309-2025-27.2-238-254 ART I CLE I NFO Article history: Received: 06 March 2025 Revised: 27 March 2025 Accepted: 10 April 2025 Available online: 15 June 2025 Keywords: Impact treatment Nickel alloy ZhS6U Surface hardening Mechanical processing Additive manufacturing EBAM Funding The work was carried out within the framework of a grant from the Russian Science Foundation, project No. 2379-01301.The studies were carried out using equipment from the Center of Collective Use «Nanotech» of the Institute of Strength Physics and Materials Science SB RAS. ABSTRACT Introduction. Nickel alloys are widely used in the aerospace industry, but their operational characteristics require improvement through surface modifi cation. A relevant challenge is to conduct a comparative analysis of mechanical impulse processing methods for cast and additively manufactured ZhS6U alloy to optimize their properties. The purpose of this work is to investigate the infl uence of low-frequency (LF) and highfrequency (HF) impact processing on the structural-phase state and surface properties of nickel alloy ZhS6U, produced by electron beam additive manufacturing (EBAM) and casting. The research methods include microstructural analysis using optical microscopy, X-ray diff raction analysis of the phase composition, microhardness measurements, and tribological testing via scratch testing of ZhS6U alloy samples after various processing modes. Results and discussion. It is established that LF processing of the cast alloy increases the volume fraction of the strengthening γ’ phase, while HF processing forms an additional Ti2O phase. The processing of the additive alloy demonstrates more signifi cant changes: micro-strains in the crystal lattice are 1.71…2.18 times higher, micro-stresses in the surface layer are 2.09…2.73 times higher, and the microhardness of the processed surface of the additively manufactured ZhS6U alloy is 8…16% higher compared to the cast material. Optimal processing modes are identifi ed to be: 40 seconds for LF and 20 minutes for HF, providing a minimum friction coeffi cient of 0.075. Conclusions. Mechanical impulse processing eff ectively hardens the surface of nickel alloy ZhS6U fabricated by diff erent methods. The application of the developed approaches is recommended to improve the performance characteristics of parts in the aerospace and mechanical engineering industries. Further research is required on the cyclic stability of modifi ed structures after mechanical impulse processing in various frequency ranges. For citation: Vorontsov A.V., Panfi lov A.O., Nikolaeva A.V., Cheremnov A.V., Knyazhev E.O. Eff ect of impact processing on the structure and properties of nickel alloy ZhS6U produced by casting and electron beam additive manufacturing. Obrabotka metallov (tekhnologiya, oborudovanie, instrumenty) = Metal Working and Material Science, 2025, vol. 27, no. 2, pp. 238–254. DOI: 10.17212/1994-6309-2025-27.2238-254. (In Russian). ______ * Corresponding author Vorontsov Andrey V., Ph.D. (Engineering), Researcher Institute of Strength Physics and Materials Sciences SB RAS, 2/4, pr. Akademicheskii, 634055, Tomsk, Russian Federation Tel.: +7 983 239 3417, e-mail: vav@ispms.ru References 1. Pollock T.M., Tin S. Nickel-based superalloys for advanced turbine engines: chemistry, microstructure and properties. Journal of Propulsion and Power, 2006, vol. 22 (2), pp. 361–374. DOI: 10.2514/1.18239. 2. Semiatin S.L., McClary K.E., Rollett A.D., Roberts C.G., Payton E.J., Zhang F., Gabb T.P. Microstructure evolution during supersolvus heat treatment of a powder metallurgy nickel-base superalloy. Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 2012, vol. 43, pp. 1649–1661. DOI: 10.1007/ s11661-011-1035-y.
RkJQdWJsaXNoZXIy MTk0ODM1