Abstract
The method of structural analysis was used to study the structure of coatings obtained by non-vacuum electron beam deposition of boron-containing powder mixture. It is shown that a complicated structure containing borides and eutectic formed during the process of surfacing. The high concentration of borides in the surface layers promoted twofold increase in wear resistance of deposited coatings.
Keywords: high-speed heating, boron, coating, wear resistance
References
1. Крукович М. Г., Прусаков Б. А., Сизов И. Г. Пластичность борированных слоев. М. : Физматлит, 2010. 384 с.
2. Полетика И.М., Крылова Т.А., Макаров С.А. Использование электронно-лучевой обработки для создания упрочняющих покрытий // Известия Томского политехнического университета. 2011. Т. 319. № 2. С. 94-98.
3. Teplykh A.M., Golkovskiy M.G., Bataev A.A. Boride Coatings Structure and Properties, Produced by Atmospheric Electron-Beam Cladding // Advanced Materials Research Vols. 287-290 (2011) pp 26-31.
4. Теплых А.М. Использование электронно-лучевого нагрева для формирования на сталях износостойких поверхностных слоев // Обработка металлов. Технология. Оборудование. Инструменты. - 2011. - № 3(52). - С. 91-94.